Hard Coated Polycarbonate sheet for windscreen windshield

Hard Coated Polycarbonate sheet for windscreen windshield,Construction & Real Estate,Plastic Building Materials

INQUIRY PRECISE INQUIRY

Description

Overview

Quick Details

Place of Origin:: Zhejiang, China

Brand Name:: Zhengshun

Model Number:: UL11CT

Type:: Sun Sheets & PC Embossed Sheets

Product name:: Hard Coated Polycarbonate sheet for windscreen windshield

Material:: Polycarbonate

Certification:: ISO9001 UL CE ROHS SGS

Size:: 1220mm*2440mm

MOQ:: 2 tons

Thickness:: 1.5mm to 18mm

Sample:: for free

Hardness:: HB

Warranty:: 10years

Supply Ability

Supply Ability:: 3500 Ton/Tons per Year Hard Coated Polycarbonate sheet for windscreen windshield

Packaging & Delivery

Packaging Details: PE protective film on both side. Kraft paper out size and pallet

Port: NINGBO

Lead Time :: within 5-7 days after receive 30% deposit

Hard coated

Hard coated polycarbonate sheet

Abrasion-resistant Polycarbonate sheet has a hard-coated surface treatment applied to one side or both sides of the sheet. The proprietary hard-coat also provides chemical resistance and long lasting outdoor weathering performance. This product is available in clear as well as transparent solar gray and bronze.

Abrasion-resistant Polycarbonate sheet is used extensively in school and factory glazing for protection against both accidental breakage and deliberate vandalism. In manufacturing environments, this high-impact material excels in applications like machine guards, noise abatement shields, clear work station partitions, freight doors and other in-plant glazing.

Technical data:

Item	Property	Test Method	U/M	Value
Mechanical	Hardness 1KG	ANSI Z87.1 2010	H	1
	High velocity impact	ANSI Z87.1 2010	ft/s	>300
	Cross-Cut tape test	ISO 527	NA	Pass
	Elongation, yield	ISO 527	%	7
	Elongation, break	ISO 527	%	110
	Tensile stress, yield	ISO 527	Mpa	60
	Tensile modulus MPa	ISO 527	Mpa	2300
	Flexural strength, yield	ISO 178	Mpa	100
	Flexural modulus	ISO 178	Mpa	2500
	Izod notched impact, 20 °C	ANSI Z87.1 2010	KJ/m²	65
Physical	Gravity	ISO 1183	g/cm³	1.2
Physical	Water absorption, 24 hours	ANSI Z87.1 2010	%	0.15
Thermal	Mold shrinkage	ISO 11359	%	0.5-0.7
	Thermal expansion	ISO 11357	1/ °C	7×10-5
	Vicat Softening Temp., Rate B / 120(base sheet)	ASTM D5470	°C	150
	HDT, 0.45 MPa	ISO 11357	°C	138